摘要：依据金属第4 强度理论对铸钢模筒壁厚进行强度校核，运用JMatPro 软件进行材料力学性能的计算模拟， 结合胀裂铸钢模筒的断面分析和坯件选样拉伸试验，确定夹渣、疏松等缺陷是导致铸钢模筒强度失效的主要原因。针对 存在问题，采取优化离心机转速、把好投料质量关等措施，减少了离心铸造铸钢模筒胀裂失效故障率。

摘要：This thesis investigates the effect of bulk and local cavitation on a threedimensional ship-like box model. The fluid surrounding the structure is modeled to capture the effect of cavitation.

Abstract: Hot-tearing cracks usually form near the solidus temperature． It is caused by a combination of tensile stress and metallurgical embrittlement． In order to quantify embrittlement and to incor

To examine the e®ect of processing parameters on microstructural evolution and to obtain the excellent combination of strength and toughness, simulation of thermo-mechanical processing was conducted u

摘要：采用Ｔｈｅｒｍｏ－ｃａｌｃ热力学计算软件以及ＪＭａｔＰｒｏ分析软件对ＤＤ６镍基单晶高温合金真空感应熔炼过程中氧化物 夹杂形成的热力学条件进行了计算分析。结果表明：ＤＤ６单晶高温合金熔化和凝固过程中形成的氧化物夹杂主要为 Ａｌ２Ｏ３。热力学平衡状态下，熔化阶段和凝固阶段合金液中氧的活度分别在（３．２１～１４．０）×１０－７，（１．６３～４．８９）×１０－８ 范围内。

摘要: 在环/块对摩型磨损试验机上对比测试了不同载荷下4 种Cr8 型模具钢的干滑动磨损性能，测量磨痕宽 度，观察磨损形貌，分析磨损机制． 结果表明: 不同载荷下均有磨粒磨损，随载荷增大氧化加剧并伴有粘附磨损，高载 荷下氧化磨损的作用变大; 磨损损失体积随载荷增加而增大，磨损损失体积总量与M7C3 共晶碳化物量呈正线性关 系; 摩擦系数随载荷增加先升高后下降．

摘要：Cr3 钢是目前广泛使用的轧辊材料，其局部修复有重要意义。研究了不同预热温度和焊后缓冷 对Cr3 钢轧辊局部堆焊修复质量的影响。通过焊接工艺试验、无损探伤、焊接热模拟试验及金相分析， 证明了在Cr3 钢轧辊局部修复中，焊接热影响区的最大焊接收缩量ΔL、马氏体含量均随预热温度 的下降而增加；在预热温度相同时，ΔL 随冷速降低而降低。在350 ℃保温缓冷即可明显改善Cr3 钢组 织。通过缓冷可将

摘要：为了减轻高级别帘线钢晶界渗碳体（ＧＢＣ）的析出、提高其强度和冷拉性能，研究了Ｃｏ微合金化８０，１００级帘线钢 的显微组织及性能变化规律。用扫描电镜（ＳＥＭ）观测了不同Ｃｏ含量试样的显微组织形貌、ＧＢＣ析出及珠光体片间距； 用力学实验机测量了热加工及冷拉拔后的力学性能。

Abstract: In five-axis machining, tool orientation above a blade stream surface may lead to tool collision and a decrease in workpiece rigidity. Hence, collisionless tool orientation smoothing (TOS) b

摘　要：利用Ｔｈｅｒｍｏ－Ｃａｌｃ软件计算得出Ａｌ含量对Ｋ４１８合金的ＴＣＰ相析出规律的影响。结果表明：Ｋ４１８合金 析出相为ＭＣ相、Ｍ２３Ｃ６ 相、γ相、γ′相、σ相、μ相、α－Ｃｒ相、Ｍ３Ｂ２ 相和液相。Ａｌ质量分数在６．５％～５．５％成分范围 内，碳化物、硼化物、液相线的含量变化较小，有少量α－Ｃｒ相析出。随Ａｌ含量减少，ＴＣＰ相析出含量而减少且呈阶 段性变化，在７１０℃以下以μ相析出为主；